G60 Galvanized Coil Description
G60 is the coating grade of steel sheet after continuous hot dip plating process. G represents the "galvanized" or galvanized layer of the product. The number 60 refers to the thickness of the zinc around the steel sheet or the thickness of the entire double-sided coating. To get the amount of galvanizing on one side, you need to divide this number by two.
Galvanized steel sheet G60 is coated with molten zinc. After the continuous coating process at a speed of 600 feet per minute, the excess zinc on the steel plate is removed by high-pressure air. This is in order to produce the desired coating thickness. After cooling, the sheet is rolled into a roll, ready for manufacturing.
Scope of Application
Galvanizing products are widely used in industry, agriculture, animal husbandry and fishery, energy, transportation, chemical industry, light industry, home appliances, construction, communications, national defense and other fields.
Product Parameters
|
Product Name |
G60 Galvanized Coil |
|
Thickness |
0.12mm-3.5mm |
|
Width |
600mm-1500mm |
|
Length |
508mm/610mm, Support Customization |
|
Standard |
AISI, ASTM, DIN, JIS, GB, JIS, SUS, EN, etc. |
|
Zinc Layer |
Hot Galvanizing: 60-275g/m² |
|
Pre-galvanized: 80-275g/m² |
Chemical Composition
|
Standard |
Grade |
C |
Si |
Mn |
P |
S |
Ti |
|
Forcold Forming Chinese Standard |
DX51D+Z |
0.12 |
0.50 |
0.60 |
0.100 |
0.045 |
0.30 |
|
DX52D+Z |
0.12 |
0.50 |
0.60 |
0.100 |
0.045 |
0.30 |
|
|
DX53D+Z |
0.12 |
0.50 |
0.60 |
0.100 |
0.045 |
0.30 |
|
|
DX54D+Z |
0.12 |
0.50 |
0.60 |
0.100 |
0.045 |
0.30 |
|
|
DX56D+Z |
0.12 |
0.50 |
0.60 |
0.100 |
0.045 |
0.30 |
|
|
DX57D+Z |
0.12 |
0.50 |
0.60 |
0.100 |
0.045 |
0.30 |
|
|
Forcold Forming Japanese Standard |
SGCC |
0.15 |
0.50 |
0.80 |
0.050 |
0.030 |
0.025 |
|
SGCD1 |
0.12 |
0.50 |
0.60 |
0.040 |
0.030 |
0.025 |
|
|
SGCD3 |
0.08 |
0.50 |
0.45 |
0.030 |
0.030 |
0.025 |
|
|
SGCD4 |
0.06 |
0.50 |
0.45 |
0.030 |
0.030 |
0.025 |
|
|
For Structure Japanese Standard |
SGC340 |
0.25 |
0.50 |
1.70 |
0.200 |
0.035 |
0.025 |
|
SGC400 |
0.25 |
0.50 |
1.70 |
0.200 |
0.035 |
0.150 |
|
|
SGC490 |
0.30 |
0.50 |
2.00 |
0.200 |
0.035 |
0.025 |
|
|
SGC510 |
0.30 |
0.50 |
2.50 |
0.200 |
0.035 |
0.025 |
|
|
For Structure AISI Standard |
S220GD+Z |
0.20 |
0.60 |
0.70 |
0.100 |
0.045 |
0.025 |
|
S250GD+Z |
0.20 |
0.60 |
0.70 |
0.100 |
0.045 |
0.025 |
|
|
S280GD+Z |
0.20 |
0.60 |
0.70 |
0.100 |
0.045 |
0.025 |
|
|
S320GD+Z |
0.20 |
0.60 |
0.70 |
0.100 |
0.045 |
0.025 |
|
|
S350GD+Z |
0.20 |
0.60 |
0.70 |
0.100 |
0.045 |
0.150 |
|
|
S550GD+Z |
0.20 |
0.60 |
0.70 |
0.100 |
0.045 |
0.150 |
Mechanical Properties
|
Grade |
Yield Strength MPa≥ |
Tensile Strength MPa≥ |
Elongation A%≥ |
|
DX51D Z/ZM/AZ/AM |
240-380 |
270-500 |
22 |
|
DX52D Z/ZM/AZ/AM |
140-300 |
270-420 |
26 |
|
DX53D Z/ZM/AZ/AM |
140-260 |
270-380 |
30 |
|
DX54D Z/ZM/AZ/AM |
120-220 |
260-350 |
36 |
|
S220GD Z/ZM/AM |
220 |
300 |
20 |
|
S250GD Z/ZM/AZ/AM |
250 |
330 |
19 |
|
S280GD Z/ZM/AM |
280 |
360 |
18 |
|
S300GD A/AM |
300 |
380 |
18 |
|
S320GD Z/ZM/AM |
320 |
390 |
17 |
|
S350GD Z/ZM/AZ/AM |
350 |
420 |
16 |
|
S450GD A/AM |
450 |
480 |
15 |
|
S550GD Z/ZM/AZ/AM |
550 |
550 |
- |
Galvanized Surface Selection
|
Zero Spangle |
Minimized Spangle |
Normal Spangle |
Large Spangle |
|
|
|
|
|
|
Use of The Environment |
Recommended Zinc Thickness |
|
Indoor Use |
Z10 or Z12 (100g/㎡or 120g/㎡) |
|
Suburbs |
Z20 and Painting (200g/㎡) |
|
Urban or Industrial Area |
Z27 (270g/㎡) or G90 (US Standard) and painted |
|
Coastal Area |
Thicker than Z27 (270g/㎡) or G90 (US Standard) and painted |
|
Punch or Deep Drawing Application |
Thicker than Z27 (270grams/㎡) or G90 (US Standard) avoid coating peeling after stamping |
|
Surface Treatment Type |
Code |
Features |
|
Chromic Acid Treatment |
C |
Good corrosion resistance, suitable for bare state |
|
Chromic Acid Treatment+Oiling |
S |
Good corrosion resistance |
|
Phosphoric Acid Treatment (Including Sealing Treatment) |
P |
Have a certain corrosion resistance, good paint performance |
|
Phosphoric Acid Treatment (Including Sealing Treatment)+Oiling |
Q |
Has a certain corrosion resistance, good paint performance, prevent rust during transportation and storage |
|
Phosphoric Acid Treatment (Excluding Sealing Treatment) |
T |
Have a certain corrosion resistance, good paint performance |
|
Phosphoric Acid Treatment (Excluding Sealing Treatment)+Oiling |
V |
Has a certain corrosion resistance, good paint performance, and prevent rust |
|
Oiling |
O |
Prevent rust during transportation and storage |
|
No Treatment |
M |
Suitable for immediate painting |
Material Comparison
|
Chinese Standard |
Japan Standard |
European Standard |
|
DX51D Z/DC51D Z (CR) |
SGCC |
DX51D Z |
|
DX52D Z/DC52D Z |
SGCD1 |
DX52D With |
|
DX53D Z/DC53D Z/DX54D Z/DC54D Z |
SGCD2/SGCD3 |
DX53D Z/DX54D Z |
|
S220/250/280/320/350/550GD Z |
SGC340/400/440/490/570 |
S220/250/280/320/350GD Z |
|
DX51D Z/DD51D Z (HR) |
SGHC |
DX51D Z |
Packing And Delivery
Our advantage
experience
Many years of steel experience
01
cooperate
Good cooperative relationship
02
Source
Stable source
03
R&D
Gorgeous R & D strength
04
quality
Reliable quality assurance
05
test
Strict quality test
06
Production
CUSTOMER VISIT
HONOR
Customer communication
Partner
COMMON PROBLEM
FACTORY
APPLICATION SCENARIOS
Oil field
Aircraft manufacturing
Train manufacturing
Ship manufacturing
Power industry
Construction industry
GET A FREE QUOTE
RELATED PRODUCTS
Copyright ©